| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
成型收缩率 |
纵向 |
|
ASTM D-570 |
1.8-2.1 |
% |
| 横向 |
|
ASTM D-570 |
- |
% |
| 机械性能 |
拉伸屈服应力 |
122℃ |
ASTM D-638 |
21 |
MPa |
| 弯曲强度 |
23℃ |
ASTM D-790 |
105 |
MPa |
| 弯曲模量 |
100℃ |
ASTM D-790 |
900 |
MPa |
| 悬臂梁缺口冲击强度 |
23℃ |
ASTM D-256 |
75 |
J/m |
| 拉伸断裂应变 |
70℃ |
ASTM D-638 |
>60 |
% |
| 弯曲强度 |
-55℃ |
ASTM D-790 |
177 |
MPa |
| 洛氏硬度 |
|
ASTM D-785R |
121 |
|
| 拉伸屈服应力 |
100℃ |
ASTM D-638 |
28 |
MPa |
| 弯曲模量 |
-55℃ |
ASTM D-790 |
4330 |
MPa |
| 弯曲强度 |
122℃ |
ASTM D-790 |
25 |
MPa |
| 悬臂梁无缺口冲击强度 |
23℃ |
ASTM D-256 |
>1500 |
J/m |
| 拉伸断裂应变 |
23℃ |
ASTM D-638 |
56 |
% |
| 弯曲模量 |
23℃ |
ASTM D-790 |
3270 |
MPa |
| 弯曲模量 |
70℃ |
ASTM D-790 |
1480 |
MPa |
| 弯曲强度 |
70℃ |
ASTM D-790 |
54 |
MPa |
| 弯曲强度 |
100℃ |
ASTM D-790 |
35 |
MPa |
| 压缩应力 |
23℃,10%变形 |
ASTM D-695 |
105 |
MPa |
| 洛氏硬度 |
|
ASTM D-785M |
87 |
|
| 拉伸断裂应变 |
100℃ |
ASTM D-638 |
>60 |
% |
| 拉伸断裂应变 |
122℃ |
ASTM D-638 |
>60 |
% |
| 拉伸屈服应力 |
-55℃ |
ASTM D-638 |
109 |
MPa |
| 拉伸断裂应变 |
-55℃ |
ASTM D-638 |
29 |
% |
| 悬臂梁缺口冲击强度 |
23℃ |
ASTM D-256 |
68 |
J/m |
| 弯曲模量 |
122℃ |
ASTM D-790 |
630 |
MPa |
| 压缩应力 |
23℃,1%变形 |
ASTM D-695 |
28 |
MPa |
| 拉伸屈服应力 |
23℃ |
ASTM D-638 |
71 |
MPa |
| 剪切强度 |
23℃ |
ASTM D-732 |
64 |
MPa |
| 拉伸屈服应力 |
70℃ |
ASTM D-638 |
45 |
MPa |
| 电气性能 |
体积电阻率 |
23℃ |
ASTM D-257 |
1015 |
Ωm |
| 热性能 |
融解温度 |
|
ASTM D-2133 |
175 |
℃ |
| 热变形温度 |
0.46MPa |
ASTM D-648 |
168 |
℃ |
| 热变形温度 |
1.82MPa |
ASTM D-648 |
125 |
℃ |
| 其它性能 |
比重 |
23℃ |
ASTM D-792 |
1.42 |
MPa |
| 吸水率 |
|
ASTM D-570 |
0.36 |
|
| 线性膨胀系数 |
-40～29 |
ASTM D-696 |
10.1 |
10-5m/m℃ |
| 线性膨胀系数 |
29～60 |
ASTM D-696 |
12.3 |
10-5m/m℃ |
| 线性膨胀系数 |
60～104 |
ASTM D-696 |
14.1 |
10-5m/m℃ |
| 线性膨胀系数 |
104～150 |
ASTM D-696 |
15.5 |
10-5m/m℃ |